Polyester film composite material (PET composite film)
Article From：Xuchang Eric Insulation Products Co., Ltd
Polyester film composite material (PET composite film)
1. Product characteristics and scope of application
1.1 Product model Eric662 polyester film composite material
thickness，mm |
width,mm(Supplied in rolls, special specifications to be negotiated separately） |
|||
|
0.5 |
800 |
1000 |
1020 |
1200 |
|
1.1 |
800 |
1000 |
1020 |
1200 |
1.2 This product is a composite material of polyester film compounded by F grade adhesive hot rail. It has the characteristics of no creepage, small partial discharge, high pressure resistance, high mechanical strength, no deformation, no layering, and anti-aging.
1.3 This product is suitable for the insulation cylinder of dry-type transformers and is an ideal product to replace glass cloth insulation cylinder. It is placed between dry-type transformers and low-voltage coils to increase insulation strength, effectively reduce the spacing between high and low-voltage coils, reduce the volume of transformer high-voltage coils, and reduce the material cost of transformer coils. This product is also suitable for insulation between motor slots.
1.4 Technical requirements Appearance: The surface is bright, uniform, free of impurities, holes, and contamination, without layering, and without bubbles.
2. Executive standard: Enterprise standard Eric-662-2006
Note 1: The performance indicators of products with special specifications shall be mutually agreed upon by both the supply and demand parties.
3. Test method:
Appearance: visible to the naked eye.
Other performance tests were conducted according to the JB/T1496-74 Organic Thin Film Test Method.
4 Inspection rules, marking, packaging, transportation, and storage
The factory test items are items 1, 2, 3, 4, and 5 in the table
Other requirements should comply with the provisions of JB/T1496-74 "Definitions and General Requirements for Organic Films".
Storage conditions: It should be stored in a dry, clean, and well ventilated place not exceeding 35 ℃, and should not be near fire sources, heating, and avoid direct sunlight.
Storage period: twelve months at room temperature.
1.3 This product is suitable for the insulation cylinder of dry-type transformers and is an ideal product to replace glass cloth insulation cylinder. It is placed between dry-type transformers and low-voltage coils to increase insulation strength, effectively reduce the spacing between high and low-voltage coils, reduce the volume of transformer high-voltage coils, and reduce the material cost of transformer coils. This product is also suitable for insulation between motor slots.
1.4 Technical requirements Appearance: The surface is bright, uniform, free of impurities, holes, and contamination, without layering, and without bubbles.
2. Executive standard: Enterprise standard Eric-662-2006
Note 1: The performance indicators of products with special specifications shall be mutually agreed upon by both the supply and demand parties.
3. Test method:
Appearance: visible to the naked eye.
Other performance tests were conducted according to the JB/T1496-74 Organic Thin Film Test Method.
4 Inspection rules, marking, packaging, transportation, and storage
The factory test items are items 1, 2, 3, 4, and 5 in the table
Other requirements should comply with the provisions of JB/T1496-74 "Definitions and General Requirements for Organic Films".
Storage conditions: It should be stored in a dry, clean, and well ventilated place not exceeding 35 ℃, and should not be near fire sources, heating, and avoid direct sunlight.
Storage period: twelve months at room temperature.